Effect of resin cement selection on the microtensile bond strength of adhesively veneered 3Y-TZP
作者: Zhao, Jing1,2; Wang, Xinzhi1; Si, Wenjie3; Shen, Zhijian2,3
关键词: adhesion ; bond strength ; microtensile ; resin cement ; zirconium oxide
刊名: ACTA ODONTOLOGICA SCANDINAVICA
发表日期: 2013-09-01
DOI: 10.3109/00016357.2012.749516
卷: 71, 期:5, 页:1105-1111
收录类别: SCI
文章类型: Article
WOS标题词: Science & Technology
类目[WOS]: Dentistry, Oral Surgery & Medicine
研究领域[WOS]: Dentistry, Oral Surgery & Medicine
关键词[WOS]: FIXED PARTIAL DENTURES ; OF-THE-LITERATURE ; SURFACE TREATMENTS ; DENTAL PROSTHESES ; ZIRCONIA ; CERAMICS ; RESTORATIONS ; TRANSLUCENCY ; INTERLAYERS ; DURABILITY
英文摘要:

Objective. The aim of this study was to investigate the effect of resin cement selection on the microtensile bond strength (mu TBS) of adhesively veneered 3Y-TZP. Materials and methods. 3Y-TZP discs were fabricated from commercial powders and treated by sandblasting and zirconia primer. Porcelain discs were sectioned from a feldspathic block and conditioned with 5% HF and silane agent. Pre-treated surfaces of zirconia and porcelain discs were bonded together using one of the three following resin cements: Multilink N (MN), Panavia F (PA) or RelyX Unicem (RU), respectively. After light-curing the joined discs were cut into microbars where 15 microbars per group were randomly chosen for mu TBS test until failure occurred (24 h storage in water in advance, crosshead speed of 0.5 mm/min). The data were analysed by one-way ANOVA and Tukey′s test (p < 0.05). Fractured zirconia surfaces were examined using both a stereomicroscope and scanning electron microscope to identify the failure mode. Results. Significant differences in the mu TBS values among three groups were found (p < 0.001) and the descending order was PA, RU and MN. No zirconia or feldspathic failure occurred, but the zirconia/cement interfaces suffered from fracture for all samples. Cement cohesive failure and/or feldspathic/cement interfacial failure sometimes were involved. Failures were mainly adhesive for RU, while they were mixed for MN and PA. Conclusion. When using the adhesive veneering method, Panavia F offers better bond strength than Multilink N or RelyX Unicem, which is probably due to the content of the 10-methacryloyloxydecyl dihydrogenphosphate (10-MDP) monomer.

语种: 英语
项目资助者: China Scholarship Council (CSC)
WOS记录号: WOS:000324258100012
Citation statistics:
内容类型: 期刊论文
URI标识: http://ir.bjmu.edu.cn/handle/400002259/54023
Appears in Collections:北京大学口腔医学院_口腔修复科_期刊论文

Files in This Item:

There are no files associated with this item.


作者单位: 1.Peking Univ, Sch & Hosp Stomatol, Dept Prosthodont, Beijing 100081, Peoples R China
2.Stockholm Univ, Arrhenius Lab, Dept Mat & Environm Chem, S-10691 Stockholm, Sweden
3.Tsinghua Univ, Dept Mat Sci & Engn, Beijing 100084, Peoples R China

Recommended Citation:
Zhao, Jing,Wang, Xinzhi,Si, Wenjie,et al. Effect of resin cement selection on the microtensile bond strength of adhesively veneered 3Y-TZP[J]. ACTA ODONTOLOGICA SCANDINAVICA,2013,71(5):1105-1111.
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[Zhao, Jing]'s Articles
[Wang, Xinzhi]'s Articles
[Si, Wenjie]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[Zhao, Jing]‘s Articles
[Wang, Xinzhi]‘s Articles
[Si, Wenjie]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2017  北京大学医学部 - Feedback
Powered by CSpace