Novel method to measure enamel surface porosity with hydrogen peroxide bleaching
作者: Yang, Zhiyu1; Zou, Mingjian2; Lin, Xinhui2; Yang, Xiaoda1; Li, Na2; Wang, Kui1
刊名: AMERICAN JOURNAL OF DENTISTRY
发表日期: 2009-10-01
卷: 22, 期:5, 页:283-289
收录类别: SCI
文章类型: Article
WOS标题词: Science & Technology
类目[WOS]: Dentistry, Oral Surgery & Medicine
研究领域[WOS]: Dentistry, Oral Surgery & Medicine
关键词[WOS]: IN-VITRO ; BOVINE ENAMEL ; RESTORATIVE MATERIALS ; MICROHARDNESS ; DENTIN ; AGENTS ; GEL ; SEM
英文摘要:

Purpose: To establish methods to quantitate the physical surface change, not the chemical color bleaching change, of enamel occurring with hydrogen peroxide treatment in solution and commercially available plastic strips. Methods: Bovine enamel was polished to a sound, uniform, optical flat, white subsurface that was used as the initial substrate for all substrate modification, treatment and instrumental measurement using digital photography-image analysis, SEM and profilometry. Sound enamel was treated with 10, 20 and 30% solutions of hydrogen peroxide. Plastic strips were used to treat both sound and acid modified enamel surfaces. Etched enamel, similar to a 10-second exposure to lemon juice, was treated with 0.5, 1, 3, 5, 10, and 15% hydrogen peroxide for 24-hour exposure at 37 degrees C to obtain a dose response curve to this modified enamel. Results: The digital photography-image analysis system and scanning electron microscopy (SEM) were effective in detecting enamel surface porosity and structure disruptive changes, respectively. Plastic strip treatment of both sound and etched enamel produced little surface change. Measurable surface change of etched enamel was detected with as low as 1% hydrogen peroxide in solution. The surface change with 15% hydrogen peroxide was statistically significant. Dye uptake as measured by image analysis indicated an increase in surface porosity that was more evident with the acid modified surface. SEM studies were consistent with this observation. (Am J Dent 2009;22:283-289).

语种: 英语
WOS记录号: WOS:000273958100008
Citation statistics:
内容类型: 期刊论文
URI标识: http://ir.bjmu.edu.cn/handle/400002259/56325
Appears in Collections:北京大学药学院_期刊论文

Files in This Item:

There are no files associated with this item.


作者单位: 1.Peking Univ, Hlth Sci Ctr, Sch Pharmaceut Sci, Beijing 100083, Peoples R China
2.Peking Univ, Coll Chem & Mol Engn, Beijing 100083, Peoples R China

Recommended Citation:
Yang, Zhiyu,Zou, Mingjian,Lin, Xinhui,et al. Novel method to measure enamel surface porosity with hydrogen peroxide bleaching[J]. AMERICAN JOURNAL OF DENTISTRY,2009,22(5):283-289.
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[Yang, Zhiyu]'s Articles
[Zou, Mingjian]'s Articles
[Lin, Xinhui]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[Yang, Zhiyu]‘s Articles
[Zou, Mingjian]‘s Articles
[Lin, Xinhui]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2017  北京大学医学部 - Feedback
Powered by CSpace