The development of binary Mg-Ca alloys for use as biodegradable materials within bone
Li, Zijian1,2; Gu, Xunan1; Lou, Siquan2; Zheng, Yufeng1
关键词Mg-Ca alloy biocorrosion biocompatibility implant materials hydroxyapatite
刊名BIOMATERIALS
2008-04-01
DOI10.1016/j.biomaterials.2007.12.021
29期:10页:1329-1344
收录类别SCI
文章类型Article
WOS标题词Science & Technology
类目[WOS]Engineering, Biomedical ; Materials Science, Biomaterials
研究领域[WOS]Engineering ; Materials Science
关键词[WOS]SIMULATED BODY-FLUID ; IN-VIVO CORROSION ; MAGNESIUM ALLOYS ; PURE MAGNESIUM ; CALCIUM-PHOSPHATE ; PART I ; BEHAVIOR ; APATITE ; TITANIUM ; BIOMATERIALS
英文摘要

Binary Mg-Ca alloys with various Ca contents were fabricated under different working conditions. X-ray diffraction (XRD) analysis and optical microscopy observations showed that Mg-xCa (x = 1-3 wt%) alloys were composed of two phases, alpha(Mg) and Mg(2)Ca. The results of tensile tests and in vitro corrosion tests indicated that the mechanical properties could be adjusted by controlling the Ca content and processing treatment. The yield strength (YS), ultimate tensile strength (UTS) and elongation decreased with increasing Ca content. The UTS and elongation of as-cast Mg-1Ca alloy (71.38 +/- 3.01 MPa and 1.87 +/- 0.14%) were largely improved after hot rolling (166.7 +/- 3.01 MPa and 3 +/- 0.78%) and hot extrusion (239.63 +/- 7.21 MPa and 10.63 +/- 0.64%). The in vitro corrosion test in simulated body fluid (SBF) indicated that the microstructure and working history of Mg-xCa alloys strongly affected their corrosion behaviors. An increasing content of Mg(2)Ca phase led to a higher corrosion rate whereas hot rolling and hot extrusion could reduce it. The cytotoxicity evaluation using L-929 cells revealed that Mg-1Ca alloy did not induce toxicity to cells, and the viability of cells for Mg-1Ca alloy extraction medium was better than that of control. Moreover, Mg-1Ca alloy pins, with commercial pure Ti pins as control, were implanted into the left and right rabbit femoral shafts, respectively, and observed for 1, 2 and 3 months. High activity of ostroblast and osteocytes were observed around the Mg-1Ca alloy pins as shown by hematoxylin and eosin stained tissue sections. Radiographic examination revealed that the Mg-1Ca alloy pins gradually degraded in vivo within 90 days and the newly formed bone was clearly seen at month 3. Both the in vitro and in vivo corrosion suggested that a mixture of Mg(OH)(2) and hydroxyapatite formed on the surface of Mg-1Ca alloy with the extension of immersion/implantation time. In addition, no significant difference (p > 0.05) of serum magnesium was detected at different degradation stages. All these results revealed that Mg-1Ca alloy had the acceptable biocompatibility as a new kind of biodegradable implant material. Based on the above results, a solid alloy/liquid solution interface model was also proposed to interpret the biocorrosion process and the associated hydroxyapatite mineralization. (c) 2007 Elsevier Ltd. All rights reserved.

语种英语
WOS记录号WOS:000253406300005
Citation statistics
Cited Times:750[WOS]   [WOS Record]     [Related Records in WOS]
文献类型期刊论文
条目标识符http://ir.bjmu.edu.cn/handle/400002259/61696
Collection北京大学第三临床医学院_骨科
北京大学第三临床医学院_心血管内科
作者单位1.Peking Univ, Coll Engn, Dept Adv Mat & Nanotechnol, LTCS, Beijing 100871, Peoples R China
2.Peking Univ, Hosp 3, Dept Orthoped, Beijing 100083, Peoples R China
Recommended Citation
GB/T 7714
Li, Zijian,Gu, Xunan,Lou, Siquan,et al. The development of binary Mg-Ca alloys for use as biodegradable materials within bone[J]. BIOMATERIALS,2008,29(10):1329-1344.
APA Li, Zijian,Gu, Xunan,Lou, Siquan,&Zheng, Yufeng.(2008).The development of binary Mg-Ca alloys for use as biodegradable materials within bone.BIOMATERIALS,29(10),1329-1344.
MLA Li, Zijian,et al."The development of binary Mg-Ca alloys for use as biodegradable materials within bone".BIOMATERIALS 29.10(2008):1329-1344.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
谷歌学术
谷歌学术Similar articles in
[Li, Zijian]'s Articles
[Gu, Xunan]'s Articles
[Lou, Siquan]'s Articles
百度学术
百度学术Similar articles in
[Li, Zijian]'s Articles
[Gu, Xunan]'s Articles
[Lou, Siquan]'s Articles
必应学术
必应学术Similar articles in
[Li, Zijian]'s Articles
[Gu, Xunan]'s Articles
[Lou, Siquan]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.