Fluoride release/uptake from newer glass-ionomer cements used with the ART approach
作者: Gao, W; Smales, RJ; Gale, MS
刊名: AMERICAN JOURNAL OF DENTISTRY
发表日期: 2000-08-01
卷: 13, 期:4, 页:201-204
收录类别: SCI
文章类型: Article
WOS标题词: Science & Technology
类目[WOS]: Dentistry, Oral Surgery & Medicine
研究领域[WOS]: Dentistry, Oral Surgery & Medicine
关键词[WOS]: RESTORATIVE MATERIALS ; SHORT-TERM ; EXPOSURE ; INVITRO ; SALIVA ; NAF
英文摘要:

Purpose: To determine the fluoride ion release/uptake of two conventional glass-ionomer cements (GICs) manufactured for use with the ART approach (Fuji IX GP, Ketac-Molar), as compared with that of a resin-modified GIC (Fuji II LC). Materials and Methods: 15 specimens of each material were prepared and placed in vials with artificial saliva and stored at 37 degreesC. The solution was replaced weekly for 6 wks, and the fluoride ions released were measured in ppm each week. After 6 wks, the 15 specimens of each material were divided into three equal groups and placed into three fluoride recharging agents (1.23% APF gel, 1.1% neutral NaF and 0.001% CaF2) for 4 min at 23 degreesC. Fluoride ion measurements of the recharged specimens were carried out at 1 day, 2 days, then weekly for another 6 wks. Results: All freshly-mixed specimens showed the highest fluoride ion release after 1 week, then the release rates dropped quickly to become largely stabilized after 3 wks. After one 4-min exposure to APF gel the initial fluoride ion release increased significantly for all materials. The highest rates were during the first day, but then dropped very quickly to again become largely stabilized after usually 3 wks. Exposure to NaF and CaF2 did not usually result in significantly sustained fluoride ion release by any material. The order of release/uptake for all three agents was Fuji II LC > Fuji IX GP > Ketac-Molar. The mechanism of fluoride ion release after the application of different fluoride recharging agents is not clear. It may occur partly by washout of recharge agents that are retained in the pores and cracks of the restorative materials, for APF gel is viscous and difficult to wash off completely with deionized water; by erosion of surfaces by low pH agents, or by the subsequent release of fluoride ions from within the cement matrix.

语种: 英语
WOS记录号: WOS:000165880700008
Citation statistics:
内容类型: 期刊论文
URI标识: http://ir.bjmu.edu.cn/handle/400002259/64973
Appears in Collections:北京大学口腔医学院_口腔修复科_期刊论文

Files in This Item:

There are no files associated with this item.


作者单位: 1.Beijing Med Univ, Sch Stomatol, Dept Prosthodont, Beijing, Peoples R China
2.Univ Hong Kong, Fac Dent, Hong Kong, Hong Kong, Peoples R China

Recommended Citation:
Gao, W,Smales, RJ,Gale, MS. Fluoride release/uptake from newer glass-ionomer cements used with the ART approach[J]. AMERICAN JOURNAL OF DENTISTRY,2000,13(4):201-204.
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[Gao, W]'s Articles
[Smales, RJ]'s Articles
[Gale, MS]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[Gao, W]‘s Articles
[Smales, RJ]‘s Articles
[Gale, MS]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  北京大学医学部 - Feedback
Powered by CSpace